产品 · 参数
| 铬钼合金钢标准规范 Standard Specification for Cr-Mo Alloy Steel | ||||||||
| 参考标准 Reference Standard | 化学成分 Nominal Chemical Composition (W%) | |||||||
| C | Si | Mn | P | S | Ni | Cr | Mo | |
| AS 2074/L2A | 0.45-0.55 | ≤0.75 | 0.50-1.00 | ≤0.04 | ≤0.04 | - | 0.80-1.20 | - |
| AS 2074/L2B | 0.55-0.65 | ≤0.75 | 0.50-1.00 | ≤0.04 | ≤0.04 | - | 0.80-1.50 | 0.2-0.4 |
| AS 2074/L2C | 0.70-0.90 | ≤0.75 | 0.50-1.20 | ≤0.04 | ≤0.04 | - | 1.30-2.40 | 0.2-0.4 |
| ZG42Cr2Si2MnMo | 0.38-0.48 | 1.5-1.8 | 0.8-1.2 | ≤0.04 | ≤0.04 | - | 1.8-2.2 | 0.2-0.6 |
| ZG45Cr2Mo | 0.40-0.48 | 0.8-1.2 | 0.4-1.0 | ≤0.04 | ≤0.04 | ≤0.5 | 1.7-2.0 | 0.8-1.2 |
| ZG30Cr5Mo | 0.25-0.35 | 0.4-1.0 | 0.5-1.2 | ≤0.04 | ≤0.04 | ≤0.5 | 4.0-6.0 | 0.2-0.8 |
| ZG40Cr5Mo(FED4A) | 0.35-0.45 | 0.4-1.0 | 0.5-1.2 | ≤0.04 | ≤0.04 | ≤0.5 | 4.0-6.0 | 0.2-0.8 |
| ZG50Cr5Mo | 0.45-0.55 | 0.4-1.0 | 0.5-1.2 | ≤0.04 | ≤0.04 | ≤0.5 | 4.0-6.0 | 0.2-0.8 |
| ZG60Cr5Mo | 0.55-0.65 | 0.4-1.0 | 0.5-1.2 | ≤0.04 | ≤0.04 | ≤0.5 | 4.0-6.0 | 0.2-0.8 |
| FMU-29 | 0.25-0.45 | 0.3-1.0 | 0.6-1.5 | ≤0.04 | ≤0.04 | - | 6.0-8.0 | 0.2-0.4 |
| FMU-11 | 0.90-1.30 | 0.3-1.0 | 0.6-1.5 | ≤0.04 | ≤0.04 | - | 11.0-13.0 | 0.3-0.5 |
| FED-13 | 0.80-1.30 | 0.4-1.2 | 0.8-1.5 | ≤0.04 | ≤0.04 | - | 11.0-13.0 | 0.4-0.8 |
| FED-14 | 1.60-2.00 | 0.4-1.2 | 0.8-1.5 | ≤0.04 | ≤0.04 | - | 11.0-13.0 | 0.6-1.0 |
性能 · 特点
产品性能
材质：铬钼合金钢
硬度：≥HB310
冲击韧性值：AK≥60J(常温，无缺口)
产品特点
球磨机衬板用于保护磨机筒体免受研磨体和矿石的直接冲击和摩擦。 同时，可以使用不同的衬板来调节研磨体的运动状态，从而增强研磨体对物料的研磨效果，提高磨机的研磨效率，增加产量，减少研磨量和金属消耗。
提供经过适当热处理工艺的合金钢半自磨机衬板铸件。
按国际标准生产高品质的水泥磨衬板：GB/T26651,GB/T8263-1999,AS2074, AS2027, DIN 1695, AISI,ASTM,JIS G 5153,NF A32401,BS4844。
根据具体工况为您选择合适的矿山磨材质，提高磨机的生产效率，减少衬板和磨球的磨耗。